| Quantity: | |
|---|---|
| PRODUCT NAME | WR-8700P |
| APPEARANCE | Whitish to light yellow viscous liquid |
| SOLID CONTENT(%) | 11±1 |
| COSOLVENT(%) | ≤1.5 |
| VISCOSITY(mPa·s/25℃) | 2000-2500 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
| Anti-yellowing | NO |
PROPERTIES
Suitable for knife coating and scrape coating.Suitable for PVC substrate material with low glossiness.Extremely low gloss and high transparency. Good anti-stickiness. Resistance to stress whitening.
Using PolyHybrid technology, good adhesion, easy molding, resistance to plasticizer migration.
OPERATION
Dry condition：120-130°C，Recommended residence time＞1min.
It must be added 0.3-1% QT-4795Y Curing Agent.
Recommended for PVC substrate material with 70-120 oil content.
Matching our WR-8781B/WR-8735P treatment agent to adjust the gloss.
CAUTION NOTES
Adding water is not recommended.Roller coating process is not recommended.
No curing agent or insufficient drying is easy to after tack, fold white and other defects.
Recoating on a treatment agent with surface tension will result in weakened the adhesive force.
Not resistant to yellowing, light base material should be used with caution.
Changes in ambient temperature will affect the construction viscosity and may result in quantity changes.
Slow and adequate drying should be paid attention to when the size of the deep grain substrate is large.
| PRODUCT NAME | WR-8700P |
| APPEARANCE | Whitish to light yellow viscous liquid |
| SOLID CONTENT(%) | 11±1 |
| COSOLVENT(%) | ≤1.5 |
| VISCOSITY(mPa·s/25℃) | 2000-2500 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
| Anti-yellowing | NO |
PROPERTIES
Suitable for knife coating and scrape coating.Suitable for PVC substrate material with low glossiness.Extremely low gloss and high transparency. Good anti-stickiness. Resistance to stress whitening.
Using PolyHybrid technology, good adhesion, easy molding, resistance to plasticizer migration.
OPERATION
Dry condition：120-130°C，Recommended residence time＞1min.
It must be added 0.3-1% QT-4795Y Curing Agent.
Recommended for PVC substrate material with 70-120 oil content.
Matching our WR-8781B/WR-8735P treatment agent to adjust the gloss.
CAUTION NOTES
Adding water is not recommended.Roller coating process is not recommended.
No curing agent or insufficient drying is easy to after tack, fold white and other defects.
Recoating on a treatment agent with surface tension will result in weakened the adhesive force.
Not resistant to yellowing, light base material should be used with caution.
Changes in ambient temperature will affect the construction viscosity and may result in quantity changes.
Slow and adequate drying should be paid attention to when the size of the deep grain substrate is large.