| Quantity: | |
|---|---|
| PRODUCT NAME | WR-8570A |
| APPEARANCE | Whitish liquid |
| SOLID CONTENT(%) | 16±1 |
| HYDROTROPICAGENT(%) | ≤6 |
| VISCOSITY(mPa·s/25℃) | 800-1200 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
| ANTI-YELLOWING | ANTI-YELLOWING |
PROPERTIES
Suitable for roll coating process. It is recommended to base the treatment before the table WR-8570A.
Good anti-stickiness; Resistance to stress whitening; Good scratch resistance; Feel smooth.
OPERATION
Dry condition：120-130°C，Recommended residence time＞1min.
It must be added 0.3-1% QT-4795Y Curing Agent.
Recommended for 70-140 oil PVC base material.
CAUTION NOTES
Adding water is not recommended.
No curing agent or insufficient drying is easy to after tack, fold white and other defects.
Recoating on a treatment agent with surface tension will result in weakened the adhesive force.
Changes in ambient temperature will affect the construction viscosity and may result in quantity changes.
| PRODUCT NAME | WR-8570A |
| APPEARANCE | Whitish liquid |
| SOLID CONTENT(%) | 16±1 |
| HYDROTROPICAGENT(%) | ≤6 |
| VISCOSITY(mPa·s/25℃) | 800-1200 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
| ANTI-YELLOWING | ANTI-YELLOWING |
PROPERTIES
Suitable for roll coating process. It is recommended to base the treatment before the table WR-8570A.
Good anti-stickiness; Resistance to stress whitening; Good scratch resistance; Feel smooth.
OPERATION
Dry condition：120-130°C，Recommended residence time＞1min.
It must be added 0.3-1% QT-4795Y Curing Agent.
Recommended for 70-140 oil PVC base material.
CAUTION NOTES
Adding water is not recommended.
No curing agent or insufficient drying is easy to after tack, fold white and other defects.
Recoating on a treatment agent with surface tension will result in weakened the adhesive force.
Changes in ambient temperature will affect the construction viscosity and may result in quantity changes.