PRODUCT NAME | WR-8520A |
APPEARANCE | Whitish liquid |
SOLID CONTENT(%) | 16±1 |
HYDROTROPICAGENT(%) | ≤6 |
VISCOSITY(mPa·s/25℃) | 1000-1500 |
FINENESS(μm) | ≤35 |
pH VALUE | 7-8 |
Anti-yellowing | Anti-yellowing |
PROPERTIES：
1. PVC Use Water Base Matt Anti-scratch Treatment Agent. Suit for roll coating.After primer treatment, then use WR-8250A.
2. High transparency.Good anti-stickiness.Good anti-scratch.Oil smooth feeling.
3. It is recommended to use the ordinary 120 mesh square table roller surface treatment. This treatment agent is prone to break white in some substrates, please test the adaptability of substrates before using.
OPERATION：
1. Dry condition：120-130°C，Recommended residence time＞1min.
2. It must be added 0.3-1% QT-4795Y Curing Agent.
3. Recommended for PVC substrates with 100-130 oil content.
4. Matching our water-based after-treatment glossy agent to adjust gloss.
CAUTION NOTES：
1. Adding water is not recommended.
2. No curing agent or insufficient drying is easy to after tack, fold white and other defects.
3. Recoating on a treatment agent with surface tension will result in weakened the adhesive force.
Changes in ambient temperature will affect the construction viscosity and may result in quantity changes.
PRODUCT NAME | WR-8520A |
APPEARANCE | Whitish liquid |
SOLID CONTENT(%) | 16±1 |
HYDROTROPICAGENT(%) | ≤6 |
VISCOSITY(mPa·s/25℃) | 1000-1500 |
FINENESS(μm) | ≤35 |
pH VALUE | 7-8 |
Anti-yellowing | Anti-yellowing |
PROPERTIES：
1. PVC Use Water Base Matt Anti-scratch Treatment Agent. Suit for roll coating.After primer treatment, then use WR-8250A.
2. High transparency.Good anti-stickiness.Good anti-scratch.Oil smooth feeling.
3. It is recommended to use the ordinary 120 mesh square table roller surface treatment. This treatment agent is prone to break white in some substrates, please test the adaptability of substrates before using.
OPERATION：
1. Dry condition：120-130°C，Recommended residence time＞1min.
2. It must be added 0.3-1% QT-4795Y Curing Agent.
3. Recommended for PVC substrates with 100-130 oil content.
4. Matching our water-based after-treatment glossy agent to adjust gloss.
CAUTION NOTES：
1. Adding water is not recommended.
2. No curing agent or insufficient drying is easy to after tack, fold white and other defects.
3. Recoating on a treatment agent with surface tension will result in weakened the adhesive force.
Changes in ambient temperature will affect the construction viscosity and may result in quantity changes.