【DESCRIPTION】
WR-8270A Water Base Skin Feeling Scratch-Resistant Matt Surface Treatment Agent
PVC leather water base polycarbonate gloss treatment agent,mainly used with our WR-8232B to adjust the gloss & matt.
Good transparency,good hydrolysis resistance.Not recommended for using alone.
| PRODUCT NAME | WR-8270A |
| APPEARANCE | Whitish liquid |
| SOLID CONTENT(%) | 14±1 |
| HYDROTROPICAGENT(%) | ≤10 |
| VISCOSITY(mPa·s/25℃) | 800-1200 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
| ANTI-YELLOWING | ANTI-YELLOWING |
【PROPERTIES】
Skin-feeling Scratch-resistant Matt surface Treatment Agent for PVC leather. Suit for roll coating.Need to be treated with primer and then used it for surface treatment.
Using technology of Organic Matt so that it's extremely low gloss and high transparency.
Good anti-viscosity, anti-stress whitening, good scratch resistance.
【OPERATION】
Dry condition：120-130°C，Recommended residence time＞40s.
It must be added 0.3-1% QT-4795Y Curing Agent.
Recommended for 70-140 oil base material.
【DESCRIPTION】
WR-8270A Water Base Skin Feeling Scratch-Resistant Matt Surface Treatment Agent
PVC leather water base polycarbonate gloss treatment agent,mainly used with our WR-8232B to adjust the gloss & matt.
Good transparency,good hydrolysis resistance.Not recommended for using alone.
| PRODUCT NAME | WR-8270A |
| APPEARANCE | Whitish liquid |
| SOLID CONTENT(%) | 14±1 |
| HYDROTROPICAGENT(%) | ≤10 |
| VISCOSITY(mPa·s/25℃) | 800-1200 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
| ANTI-YELLOWING | ANTI-YELLOWING |
【PROPERTIES】
Skin-feeling Scratch-resistant Matt surface Treatment Agent for PVC leather. Suit for roll coating.Need to be treated with primer and then used it for surface treatment.
Using technology of Organic Matt so that it's extremely low gloss and high transparency.
Good anti-viscosity, anti-stress whitening, good scratch resistance.
【OPERATION】
Dry condition：120-130°C，Recommended residence time＞40s.
It must be added 0.3-1% QT-4795Y Curing Agent.
Recommended for 70-140 oil base material.