WR-8232B PVC Use Polycarbonate Water Base Matt Scratch & Abrasion Resistant Treatment Agent
【DESCRIPTION】
| PRODUCT NAME | WR-8232B |
| APPEARANCE | Whitish liquid |
| SOLID CONTENT(%) | 17±1 |
| HYDROTROPICAGENT(%) | ≤5 |
| VISCOSITY(mPa·s/25℃) | 1000-1500 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
【PROPERTIES】
Suit for roll coating.Recommended to use for treatment before foaming,which is used WR-8232B to pretreat twice, then drying and use high temperature to suction.
Using technology of Organic Matt so that it's extremely low gloss and high transparency.
Good anti-viscosity, anti-stress whitening, good scratch resistance.Feel smooth,good abrasion resistance.
【OPERATION】
Dry condition：120-130°C，recommended residence time＞1min.
It must be added 3-5% QT-4992A curing agent.
Recommended for PVC substrates with 70-120 oil content.
WR-8232B PVC Use Polycarbonate Water Base Matt Scratch & Abrasion Resistant Treatment Agent
【DESCRIPTION】
| PRODUCT NAME | WR-8232B |
| APPEARANCE | Whitish liquid |
| SOLID CONTENT(%) | 17±1 |
| HYDROTROPICAGENT(%) | ≤5 |
| VISCOSITY(mPa·s/25℃) | 1000-1500 |
| FINENESS(μm) | ≤35 |
| pH VALUE | 7-8 |
【PROPERTIES】
Suit for roll coating.Recommended to use for treatment before foaming,which is used WR-8232B to pretreat twice, then drying and use high temperature to suction.
Using technology of Organic Matt so that it's extremely low gloss and high transparency.
Good anti-viscosity, anti-stress whitening, good scratch resistance.Feel smooth,good abrasion resistance.
【OPERATION】
Dry condition：120-130°C，recommended residence time＞1min.
It must be added 3-5% QT-4992A curing agent.
Recommended for PVC substrates with 70-120 oil content.