| Quantity: | |
|---|---|
| PRODUCT NAME | HF-0150A |
| APPEARANCE | Slightly turbidity liquid |
| MAIN COMPONENT | co-polycondensation resin |
| SOLID CONTENT(%) | 43±1 |
| VISCOSITY(mPa·s/25℃) | 1000-3000 |
| SOLVENT | MEK/TOL |
A.This agent is tumbling matt surface treatment agent, suitable for PVC & PU softleather fracturing surface treatment.After treating,the effect is rough and strong.This agent are not-temperature, intolerance to embossing, no water kneading, no solvent.
B.Fracturing resin plastic coating the top tier,coating thinly and the thickness is "0".General tracturing resin need to adjust the color, the choice of PU powder is better.The second coating,general type fabric resin,choose the releasing and tumbling resin,Stick the base cloth and leave it when it is ripe then tumbling.
C.This product at 70°C constant temperature, 3KG pressure for 4 hours, the surface of the skin may be sticky. Please test it before using.
| PRODUCT NAME | HF-0150A |
| APPEARANCE | Slightly turbidity liquid |
| MAIN COMPONENT | co-polycondensation resin |
| SOLID CONTENT(%) | 43±1 |
| VISCOSITY(mPa·s/25℃) | 1000-3000 |
| SOLVENT | MEK/TOL |
A.This agent is tumbling matt surface treatment agent, suitable for PVC & PU softleather fracturing surface treatment.After treating,the effect is rough and strong.This agent are not-temperature, intolerance to embossing, no water kneading, no solvent.
B.Fracturing resin plastic coating the top tier,coating thinly and the thickness is "0".General tracturing resin need to adjust the color, the choice of PU powder is better.The second coating,general type fabric resin,choose the releasing and tumbling resin,Stick the base cloth and leave it when it is ripe then tumbling.
C.This product at 70°C constant temperature, 3KG pressure for 4 hours, the surface of the skin may be sticky. Please test it before using.