| Quantity: | |
|---|---|
PRODUCT NAME | BF-0990A |
APPEARANCE | Light yellow liquid |
MAIN COMPONENT | PU resin |
SOLID CONTENT(%) | 25±1 |
VISCOSITY(mPa·s/25℃) | 1200-2000 |
SOLVENT | MEK/TOL |
PROPERTIES & NOTES：
使用PUType色膏或色料，色料应先用MEK溶解后加入，搅拌均匀，色料加入量一般为3-7%可根据县体要求调整；
用于PU湿式Base，Coating0.2~0.3mmP皮或湿式Base，经100~110℃烘干，再经170℃~180℃x90S加热完成；
注意:温度过高会影响发泡效果，请客户自行测试确认，如需稀释，请使用纯度合格的MEK
A. Use PU Type organic color paste or color, color should be dissolved with MEK before adding, stirring well.The usually amount of color is 3-7%, which can be adjusted according to specific requirements.
B. Using for PU wet type Base.Coating 0.2-0.3mm PU leather or wet type Base.110-120°Cto dry→170-180°C X 90s to heat.
C. Note: Too high temperature will affect the foaming effect, please test and confirm. If dilution is required, use a pure MEK.
PRODUCT NAME | BF-0990A |
APPEARANCE | Light yellow liquid |
MAIN COMPONENT | PU resin |
SOLID CONTENT(%) | 25±1 |
VISCOSITY(mPa·s/25℃) | 1200-2000 |
SOLVENT | MEK/TOL |
PROPERTIES & NOTES：
使用PUType色膏或色料，色料应先用MEK溶解后加入，搅拌均匀，色料加入量一般为3-7%可根据县体要求调整；
用于PU湿式Base，Coating0.2~0.3mmP皮或湿式Base，经100~110℃烘干，再经170℃~180℃x90S加热完成；
注意:温度过高会影响发泡效果，请客户自行测试确认，如需稀释，请使用纯度合格的MEK
A. Use PU Type organic color paste or color, color should be dissolved with MEK before adding, stirring well.The usually amount of color is 3-7%, which can be adjusted according to specific requirements.
B. Using for PU wet type Base.Coating 0.2-0.3mm PU leather or wet type Base.110-120°Cto dry→170-180°C X 90s to heat.
C. Note: Too high temperature will affect the foaming effect, please test and confirm. If dilution is required, use a pure MEK.