PRODUCT NAME | BF-0388Z |
APPEARANCE | Light yellow liquid |
MAIN COMPONENT | PU resin |
SOLID CONTENT(%) | 21±1 |
SOLVENT | MEK/TOL/BAC |
VISCOSITY(mPa·s/25℃) | 2500-3500 |
PROPERTIES & NOTES：
使PUType色音或色料，色料应先用MEK溶解后加入，搅拌均匀;
色料加入量一般为3-7%,可根据具体要求调整;
用于PU湿式Base，Coating0.2~0.3mmP皮或湿式Base，经110~120℃烘干，再经170℃~180℃x90S加热完成;
完成的皮革，可经表面处理剂处理，效果更佳;
注明:不能用DMF稀释，会影响发泡效果:本品不适用于压花、打磨工艺
A. Use PU Type organic color paste or color, color should be dissolved with MEK before adding, stirring well.
B. The usually amount of color is 3-7%, which can be adjusted according to specific requirements.
C. Using for PU wet type Base.Coating 0.2-0.3mm PU leather or wet type Base.110-120°C to dry→170-180°C X 90s to heat.
D. Please do not use DMF to diluent or it will influence the foaming effect.This product is not suitable for embossing, grinding process.
PRODUCT NAME | BF-0388Z |
APPEARANCE | Light yellow liquid |
MAIN COMPONENT | PU resin |
SOLID CONTENT(%) | 21±1 |
SOLVENT | MEK/TOL/BAC |
VISCOSITY(mPa·s/25℃) | 2500-3500 |
PROPERTIES & NOTES：
使PUType色音或色料，色料应先用MEK溶解后加入，搅拌均匀;
色料加入量一般为3-7%,可根据具体要求调整;
用于PU湿式Base，Coating0.2~0.3mmP皮或湿式Base，经110~120℃烘干，再经170℃~180℃x90S加热完成;
完成的皮革，可经表面处理剂处理，效果更佳;
注明:不能用DMF稀释，会影响发泡效果:本品不适用于压花、打磨工艺
A. Use PU Type organic color paste or color, color should be dissolved with MEK before adding, stirring well.
B. The usually amount of color is 3-7%, which can be adjusted according to specific requirements.
C. Using for PU wet type Base.Coating 0.2-0.3mm PU leather or wet type Base.110-120°C to dry→170-180°C X 90s to heat.
D. Please do not use DMF to diluent or it will influence the foaming effect.This product is not suitable for embossing, grinding process.